イオン液体を分散させたBi<sub>0.5</sub>Sb<sub>1.5</sub>Te<sub>3</sub>複合焼結体の作製とその熱電特性の評価
書誌事項
- タイトル別名
-
- Synthesis of Bi<sub>0.5</sub>Sb<sub>1.5</sub>Te<sub>3</sub> Sintered Composite with Dispersed Ionic Liquid and Investigation of their Thermoelectric Properties
- イオン液体を分散させたBi₀.₅Sb₁.₅Te₃複合焼結体の作製とその熱電特性の評価
- イオン エキタイ オ ブンサン サセタ Bi ₀.₅ Sb ₁.₅ Te ₃ フクゴウ ショウケツタイ ノ サクセイ ト ソノ ネツデントクセイ ノ ヒョウカ
この論文をさがす
抄録
<p>The sintered composite of Bi0.5Sb1.5Te3 and ionic liquid, BMImTFSI, was synthesized by sintering the mixture of Bi0.5Sb1.5Te3 powder and BMImTFSI at 573 K by hot pressing, and its microscopic structure and thermoelectric properties were investigated. The dispersed micropores, where BMImTFSI occupied, were observed by SEM observation on the cross-section of Bi0.5Sb1.5Te3-BMImTFSI sintered composite. With an increase of the amount of BMImTFSI, the Seebeck coefficient of the composite generally decreased, while the electrical resistivity increased and the electrical resistivity of the composite with 0.5 ml of BMImTFSI is about two times larger than that of Bi0.5Sb1.5Te3 with no BMImTFSI. The thermal conductivity of the composite with 0.01 ml of BMImTFSI was reduced by about 20 % compared to that of Bi0.5Sb1.5Te3 with no BMImTFSI. These results indicate that the dispersed BMImTFSI in the composite acts as a scattering center for electric carrier and phonon. As a result, the dimensionless figure of merit ZT of the composite with 0.01 ml of BMImTFSI showed a maximum value of 0.70 at 373 K, which was about 20 % larger than that of Bi0.5Sb1.5Te3 with no BMImTFSI.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 63 (8), 719-724, 2016
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206310491264
-
- NII論文ID
- 130005253112
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 027541171
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可