- Feasibility Study of High-Strength Brass Coatings by Cold Spray Process
- コールドスプレーホウ オ モチイタ コウリョク オウドウマク ケイセイ ノ ココロミ
この論文をさがす
説明
<p>Cu-Zn-based brasses possess excellent strength and corrosion resistance. However, producing bulk brass parts/bodies via conventional powder metallurgy has been difficult due to the high vapor pressure of Zn. This problem is circumvented in Cold Spray, in which solid powder particles, accelerated in a supersonic gas stream, are deposited on a substrate to form dense coatings without long exposure of powder particles to high temperature. In this study, a water-atomized Cu-Zn-Mn-Al-Fe brass powder about 30 μm in average diameter was cold sprayed with and without powder pre-annealing on an aluminum substrate in a nitrogen gas stream heated to 873 K. The as-atomized brass powder consisted predominantly of β solid solution, while the powder pre-annealed at 1023 K had both α and β solutions. Coatings with more than 3 mm in thickness and of nearly full density were produced with or without powder pre-annealing. An increase in deposition efficiency was noted with the coatings sprayed with the pre-annealed powder. Cold Spray provides a viable means for the fabrication of high-strength brass coatings.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 64 (12), 661-666, 2017
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206310839680
-
- NII論文ID
- 130006317331
- 40021422129
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 028737337
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可