- Effect of Al Addition to Ni-Cr-Mo-B Gas Atomized Powder on Age Hardening
- Al テンカ シタ Ni-Cr-Mo-Bケイ ガスアトマイズ フンマツ ノ ジコウ コウカ キョドウ
この論文をさがす
抄録
<p>The effects of Al addition to Ni-Cr-Mo-B alloy with corrosion and wear resistance on age hardening behavior were investigated. Examined compositions were Ni-22 mass% Cr-23 mass% Mo-1 mass% B without Al and with 2, 3 and 4 mass% Al. The powders with these compositions were produced by gas atomization, followed by sieving under 150 μm in particle size. Then, solution treatment was carried out at 1473 K for 7.2 ks in vacuum. Also, aging treatment at 1073 K for 14.4 ks in vacuum was carried out after the solution treatment. Both of cooling conditions after these heat treatments were air cooling. As a result, two kinds of hardening phenomena were observed. One was the hardness increase with increase of Al addition of more than 3 mass% after solution treatment by formation of Mo rich intermetallic compound. The other was age hardenability by precipitation of fine aging precipitate by Al addition of more than 2 mass%.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 64 (12), 631-637, 2017
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206310848512
-
- NII論文ID
- 130006317336
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 028737304
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可