書誌事項
- タイトル別名
-
- Hardening of Thermally Sprayed WC-CrC-Ni Cemented Carbide Layer by Friction Stir Processing
- マサツ カクハン プロセス ニ ヨル WC-CrC-Ni ヨウシャ チョウコウゴウキン ヒマク ノ コウコウドカ
この論文をさがす
説明
Friction stir processing of a thermally sprayed WC-CrC-Ni cemented carbide layer was carried out to clarify the optimum conditions for obtaining a hardened layer without any cracks and pores. Although cracks and pores were observed in the cemented carbide layer after friction stir processing at a forging load of 4.9 kN, friction stir processing at a higher forging load of 9.8 kN or 14.7 kN could eliminate these defects. The amount of pores was decreased owing to rearrangement of WC particles by the stirring effect. The cracks were suppressed by densification of the cemented carbide layer and the martensitic transformation of the SKD61 substrate during cooling. When the forging load was 14.7 kN, the hardness of the cemented carbide layer reached to 2200 HV. On the other hand, friction stir processing at 19.6 kN caused large plastic deformation of the SKD61 substrate and cracks occurred in the cemented carbide layer on the advancing side.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 62 (5), 252-257, 2015
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206311524608
-
- NII論文ID
- 130005074111
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 026438047
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可