Friction and Wear of Al2O3 against Sialon, ZrO2, Al2O3, and SUS304 in Journal Sliding Bearing Test.

DOI Web Site Web Site 1 Citations 9 References

Bibliographic Information

Other Title
  • 滑り軸受試験によるＡｌ２Ｏ３の摩擦・摩耗　　Ｓｉａｌｏｎ，ＺｒＯ２，Ａｌ２Ｏ３およびＳＵＳ３０４と組合された場合
  • スベリ ジクウケ シケン ニヨル Al2O3 ノ マサツ マモウ Sialon

Search this article

Abstract

Journal sliding bearing tests were performed under non-lubricated and water-lubricated conditions. Journals made of Al2O3 were slid against bushes made of Sialon, ZrO2, Al2O3, and SUS304 stainless steel. The Al2O3/Al2O3 combination exhibited the best performance under these test conditions. The wear amount and friction coefficient under the water-lubricated condition were smaller than those under the non-lubricated condition except for the case of Sialon/Al2O3 combination. The wear of Sialon might be increased under the influence of the hydrate formed on the sliding surface by tribochemical reaction. The wear amount of Al2O3 journal was largest in the case of SUS304/Al2O3 combination, in which the wear mode was micro-chipping. On application of Al2O3 under the water-lubricated condition, wear of Sialon in the case of Al2O3/Sialon combination, stress corrosion wear of ZrO2 in the case of Al2O3/ZrO2 combination, and wear of Al2O3 by micro-chipping in the case of Al2O3/SUS304 combination must be considered.

Journal

Citations (1)*help

See more

References(9)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top