- Effect of Sc addition on the age-hardening and precipitation behavior of Al-2.5mass%Cu alloy.
- Al-2.5%Cu合金の時効硬化と析出挙動に及ぼすSc添加の影響
- Al 2.5パーセント Cu ゴウキン ノ ジコウ コウカ ト セキシュツ キ
この論文をさがす
抄録
Age-hardening and precipitation behavior of an Al–2.5 mass%Cu–0.23 mass%Sc alloy were investigated by means of hardeness test and TEM observation. The effect of scandium on the age-hardening behavior of the Al–Cu alloy is most remarkable at the aging temperature of 573 K. Precipitates formed at 573 and 623 K in the Al–Cu–Sc alloy are the θ′–Al2Cu and Al3Sc phases. They precipitate independently in the matrix without any apparent interactions for the heterogeneous precipitation.
収録刊行物
-
- 軽金属
-
軽金属 46 (6), 275-279, 1996
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206335502720
-
- NII論文ID
- 10003793912
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK28XksVSgs7g%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3986454
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可