Effect of specimen surface on the precipitation hardening of an Al-1.2mass%Si alloy.
-
- KANADANI Teruto
- Faculty of Engineering, Okayama University of Science
-
- NAKAGAWA Keiyu
- Graduate School, Okayama University of Science
Bibliographic Information
- Other Title
-
- Al‐1.2%Si合金の析出硬化に及ぼす試料表面の影響
- Al-1.2%Si合金の析出硬化に及ぼす試料表面の影響
- Al 1.2パーセント Si ゴウキン ノ セキシュツ コウカ ニ オヨボス
Search this article
Abstract
Dependence of precipitation hardening and aged structures of an Al–1.2 mass%Si alloy on the distance from specimen surface was studied by microhardness test and transmission electron microscopy. The specimen was water-quenched from 833 K or 853 K to 273 K, held for 60 s and subsequently aged at 373 K, 423 K or 473 K. Rate of age-hardening was slower in the surface layer than in the interior when the specimen was aged at relatively low temperatures (373 K and 423 K) .However the value of maximum hardness in the surface layer became the same as that in the interior. According to the results of electron microscopy, the size of Si phase precipitates formed in the surface layer was smaller than that in the center of specimen aged at 423 K. This difference was considered to be caused by the effect of the surface as a vacancy sink which slowed down the growth of Si phase precipitates near the surface.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 47 (1), 39-43, 1997
The Japan Institute of Light Metals
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206336545792
-
- NII Article ID
- 10003794869
- 10004010574
- 10003904269
-
- NII Book ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK2sXhsVyhu7s%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL BIB ID
- 4118763
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed