- Structure and properties of rapidly solidified Al-6-8 mass%Mn-1-3 mass%Cr alloys.
- 急冷凝固法によるAl-6~8%Mn-1~3%Cr合金の組織と性質
- キュウレイ ギョウコホウ ニ ヨル Al 6 8パーセント Mn 1 3パーセント Cr ゴウキン ノ ソシキ ト セイシツ
この論文をさがす
説明
In order to assess the optimum alloying composition, rapidly solidified P/M materials were prepared for Al–Mn–Cr ternary alloys containing 6∼8 mass%Mn and 1∼3 mass%Cr. Effects of alloying composition on precipitation hardening were studied with a purpose of obtaining precipitation-hardened materials with some acceptable ductility. The critical composition to observe precipitation hardening was identified as 8.8 mass%Mn + Cr, above which hardening increased with increasing Mn + Cr. The largest hardening was observed for 7Mn–3Cr alloy containing highest Mn + Cr. CrAl7 was formed in as rapidly solidified state, and precipitation of MnAl6 occurred during hot extrusion in alloys of lower Cr content. Finally, G phase, (Mn, Cr) Al12 was formed during heating of hot-extruded materials, thereby hardening occurred when amount of G phase formation is sufficiently large. For the as-extruded P/M materials, the highest tensile strength of 480 MPa was obtained at room temperature for 7Mn–3Cr with 7% elongation. Elongation of the as-extruded P/M materials kept unchanged up to 473 K but increased appreciably at 673 K. However, the heat-treated P/M materials showed poor ductility and hence tensile strength decreased with aging time regardless of occurrence of hardening. Increases in elastic modulus were observed after precipitation heat treatment.
収録刊行物
-
- 軽金属
-
軽金属 50 (1), 12-17, 2000
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206336568192
-
- NII論文ID
- 10004548393
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DC%2BD3cXhvVymtbo%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4971129
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可