書誌事項
- タイトル別名
-
- Recycling and Environmental problem. Reinforcement of 6063 aluminum alloy cutting chips by ball milling.
- ボールミリングによる6063アルミニウム合金切削粉の高強度化
- ボール ミリング ニヨル 6063 アルミニウム ゴウキン セッサク フン ノ
この論文をさがす
説明
In order to develope a recycled material with good mechanical properties, investigations about ball milling (BM) process to the 6063 aluminum alloy cutting chips from manufacturing process of architectural products were carried out. 6063 aluminum alloys are utilized for architectural products due to their good workability and corrosion resistance, and cutting chips of 6063 aluminum alloy from its manufacturing process are produced as much as hundreds tons per year. Application of BM process to 6063 aluminum alloy cutting chips causes grain refinement and improves its mechanical properties. With the progress of BM process, grain size of cutting chips reduced as fine as 200 nm, and its Vickers hardness became as high as 140 after 259.2 ks BM process. The extruded bar made of the cutting chips ball milled for 259.2 ks showed as high as 400 MPa in tensile strength and 30% of elongation.
収録刊行物
-
- 軽金属
-
軽金属 46 (11), 602-606, 1996
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206337151360
-
- NII論文ID
- 130004481239
- 10003795808
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK28XnsFykt7g%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 4087626
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可