Effects of Mg contents on porosity formation in Al-Mg alloy DC slabs.

DOI 8 References
  • NAGAUMI Hiromi
    Nippon Light Metal Company Ltd. Nikkei Research & Development Center
  • TSUCHIYA Kiyomi
    Nippon Light Metal Company Ltd. Nikkei Research & Development Center

Bibliographic Information

Other Title
  • Ａｌ‐Ｍｇ合金ＤＣスラブのポロシティ形成に及ぼすＭｇ量の影響

Search this article

Description

The effect of Mg content on porosity in Al–Mg alloy DC slabs was investigated. In this investigation, we performed an experimental study of the amount of porosity on laboratory scale (250 mm by 400 mm cross-section) DC slabs of Al–2, 3, 4, 5and 6 mass% Mg. We clarified the relationship between porosity formation and Mg contents of the DC slab quantitatively by measuring porosity size, fractions, and number of porosity from the surface to the center of slab. The following conclusions were obtained, (1) As the Mg contents increase the initial hydrogen contents increase, and the hydrogen contents can be expressed in a quadratic of Mg contents (mass%) with good accuracy. (2) When the Mg content is less than 2 mass%, the porosity were very small and distributed uniformly from the surface to the center of the slab. (3) When the Mg content exceeds 3 mass%, the pore sizes and the fractions increase from the surface to the center of the slab. As the Mg content increases the porosity content and number increase.

Journal

References(8)*help

See more

Keywords

Details 詳細情報について

  • CRID
    1390001206337371776
  • NII Article ID
    130004481590
  • DOI
    10.2464/jilm.52.293
  • COI
    1:CAS:528:DC%2BD38XmvFWrsb8%3D
  • ISSN
    18808018
    04515994
  • Text Lang
    ja
  • Data Source
    • JaLC
    • Crossref
    • CiNii Articles
  • Abstract License Flag
    Disallowed

Report a problem

Back to top