- The temperature dependence of ductility in 5083 alloy
- 5083 ゴウキン ノ エンセイ ノ オンド イゾンセイ
この論文をさがす
抄録
Tensile tests were proceeded at temperatures from -196°to 550°C. The load-elongation curve has different shapes in accordance with rise of the testing temperature such as homogeneous deformation at low temperatures and larger deformation at elevated temperatures. Typical superplastic deformation is found at the temperatures 400°C or above. The elongation is represented by the work-hardening index n at low temperatures and by the strain-rate sensitivity index m at elevated temperatures. The elongation about 180% at 550°C is smaller than that predicted by the m-value 0.5. In such a case, coarsening and shape change of grains and a number of voids are found near the fracture surface.
収録刊行物
-
- 軽金属
-
軽金属 29 (2), 47-51, 1979
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206338429568
-
- NII論文ID
- 130004208069
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 2041446
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可