- On the diffusion brazing of Al-Si alloy castings
- Al Si ゴウキン イモノ ノ カクサン ロウセツ ニカンスルケンキュウ
この論文をさがす
抄録
The diffusion brazing process in which the liquid filler metal is formed by mutual diffusion between the brazement and the insert metal in a brazing cycle was applied to joining Al-Si alloy castings. When the brazement of Al-Si alloy castings with a copper insert metal is heated up to the ternary eutectic point of Al-Cu-Si system at 525°C, a ternary eutectic Al-27%Cu-5%Si alloy will be formed at the interface to act as a brazing filler metal. The diffusion brazing process seemed to be suitable for brazing the Al-Si alloy castings from the viewpoints of good brazability and uniform structure of brazed joint. The brass insert metal is more beneficial than copper on lowering brazing temperature.
収録刊行物
-
- 軽金属
-
軽金属 29 (3), 102-107, 1979
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206338444928
-
- NII論文ID
- 130004208080
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 2044574
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可