大気中でのTi–AlおよびTi–V合金の高温酸化とその速度論的考察

DOI Web Site 参考文献30件
  • 高橋 知司
    Department of Environmental Materials Engineering, Institute of Niihama National College of Technology
  • 南埜 宜俊
    Department of Adaptive Machine Systems, Graduate School of Engineering, Osaka University
  • 平澤 英之
    Department of Environmental Materials Engineering, Institute of Niihama National College of Technology
  • 大内 忠司
    Department of Environmental Materials Engineering, Institute of Niihama National College of Technology

書誌事項

タイトル別名
  • High-temperature oxidation and its kinetics study of Ti–Al and Ti–V alloys in air
  • タイキ チュウ デ ノ Ti-Al オヨビ Ti-V ゴウキン ノ コウオン サンカ ト ソノ ソクドロンテキ コウサツ
  • High-temperature oxidation and its kinetics study of Ti^|^ndash;Al and Ti^|^ndash;V alloys in air

この論文をさがす

抄録

The high-temperature oxidation behavior of Ti– (6–36) mass%Al alloys and Ti– (4–15) mass%V alloys have been investigated in a temperature range of 1123 to 1273 K in air. A kinetic study of the oxidation has been also carried out in Ti–6 mass%Al alloy and Ti–4 mass%V alloy. The growth rate of oxides in Ti–V alloys is larger than that in Ti–Al alloys. The oxidation products have been examined by X-ray diffraction (XRD), electron probe microanalysis (EPMA) and X-ray photoelectron spectroscopy (XPS). The Al2O3 layer is probably formed in the Ti–Al/oxides interface of the Ti–6 mass%Al alloy by means of EPMA, although only the rutile TiO2 is detected by means of XRD in the oxides of surface layer in Ti–6 mass% Al alloy and Ti–4 mass%V alloy at 1273 K. Furthermore, the TiO2 and Al2O3 are observed by XPS in surface of the above both alloys at 1123 K for 3.6 ks, but the V2O5 is not observed. It is found that the apparent activation energy (245 kJ/mol) for the oxidation experiment (TG experiment) at a constant heating rate is fairly equal to the activation energy (253 kJ/mol) for the isothermal oxidation in Ti–6 mass%Al alloys.

収録刊行物

  • 軽金属

    軽金属 63 (2), 41-48, 2013