- Effects of homogenization conditions of ingots on stress corrosion resistance of Al-Zn-Mg alloys
- Al Zn Mg ゴウキン ノ タイ オウリョク フショク ワレセイ ニ オヨ
この論文をさがす
説明
Effects of homogenization conditions of ingots on stress corrosion resistance (SCR) of Al-Zn-Mg alloy ingots, plates and extrusions were investigated.<br>(1) SCR of ingots decreased with increased homogenizing temperature.<br>(2) SCR of plates in ST-direction was independent of homogenizing conditions, but in LT-direction decreased by homogenizing at too high temperature.<br>(3) In LT-direction, SCR of plates was superior to that of ingots, but in ST-direction inferior to that of ingots.<br>(4) SCR in LT-direction of extrusions without homogenization decreased when extrusion speed was higher, while that of extrusions extruded at lower extrusion speed was independent of homogenizing conditions.<br>(5) In the structural factors depending on homogenization and hot working conditions, grain shape was a potential factor governing SCR.<br>(6) Relationship between SCR and grain shape was explained by the assumption that the higher the per-pendicular component to grain boundary of applied stress, and the flatter and the more monotonous the grain boundary, the longer the stress corrosion cracking life.
収録刊行物
-
- 軽金属
-
軽金属 26 (10), 501-509, 1976
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206339058816
-
- NII論文ID
- 130004075496
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 1732115
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可