Deformation of brazing sheets affected by the structure of core materials during brazing.

DOI Web Site 7 Citations

Bibliographic Information

Other Title
  • ブレージングシートのろう付時の変形と心材の組織との関係
  • ブレージング シート ノ ロウズケジ ノ ヘンケイ ト シンザイ ノ ソシキ

Search this article

Abstract

A basic study has been made in order to obtain a brazing sheet having a high resistance to deformation during brazing. At first, the amount of deformation at brazing temperature of 610°C was measured on several brazingsheet specimens consisting of 4343 cladding alloy (both sides cladding) and Al-1.2%Mn base core alloys having no impurity or containing a small amount of Si, Fe, Cu, Mg, etc., as a function of cold reduction of specimens. Marked deformation was observed in the Si contained specimen (Si is added to the core alloy) cold-rolled by 515% and in the Fe contained specimen with a large reduction. Then, the two sorts of deformation were studied in detail in view of reaction at the interface between solid core and liquid phase of cladding alloy. It was found that the microstructure of core alloys at brazing temperature was of great importance for the stability of interface. It was concluded that in order to get an excellent brazing sheet, the core alloy was needed to show a completely recrystallized structure having coarse and elongated grains. The Al-Mn binary specimen free from impurity would satisfy the above condition.

Journal

Citations (7)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top