- Relation between thermomechanical treatments and mechanical properties of Al-Zn-Mg-Cu base alloys
- Al Zn Mg Cuケイ ゴウキン ノ カコウ ネツ ショリ ト キカイテキ
この論文をさがす
説明
An investigation was carried out to clarify the effect of various final thermomechanical treatments (FTMT) on the mechanical properties of Al-Zn-Mg-Cu base alloys. The results are summerized as follows;<br>(1) Al-Zn-Mg-Cu alloy plates processed by FTMT exhibit better combination of strength vs. elongation as well as higher strength than those of conventionally processed plates.<br>(2) Sufficient preaging after quenching, warm deformation less than 30% and final aging at slightly lower temperature than that of conventional T6 temper are desirable in obtaining marked improvement in mechanical properties by FTMT.<br>(3) 7178 alloy processed by FTMT exhibits better combination of strength vs. elongation than that of 7075 alloy. Yield strength of 7178 alloy plates can be raised up to 70 kg/mm2 by FTMT.<br>(4) A high purity 7178 alloy processed by FTMT exhibits the same combination of strength vs. elongation as a commercial purity alloy.
収録刊行物
-
- 軽金属
-
軽金属 26 (7), 347-355, 1976
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206340367488
-
- NII論文ID
- 130004207883
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 1719040
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可