- Study on the phase diagram of Al-Si-Sr ternary alloy system.
- Al Si Sr 3ゲンケイ ジョウタイズ ノ ケンキュウ
この論文をさがす
説明
The aluminum corner of Al-Si-Sr ternary alloy system was investigated by means of inverse rate thermal analysis, identification by X-ray diffraction, EPMA analysis and microscopic observation.<br>A ternary compound SrAl2Si2, named "T", exists in this ternary system and Al-T line is considered as a quasibinary system with a eutectic point at 1.1%Si, 2.4%Sr, 645°C. The aluminium corner is divided into two regions by the Al-T quasibinary system. A ternary eutectic point was determined to locate at 575°C, 13.1%Si, 0.03% Sr, which is very close to the Al-Si binary eutectic point. The modification effect of small amount of strontium addition on Al-Si alloys can be regarded to be due to the formation of fine ternary eutectic structure. In the Al-SrAl4-T region, a ternary eutectic point was found to locate at 643°C with 1.7%Si, 2.4%Sr.
収録刊行物
-
- 軽金属
-
軽金属 35 (2), 71-78, 1985
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206340755968
-
- NII論文ID
- 130004208531
- 10003441588
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 3021575
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可