Age-hardening behavior of thermomechanically treated Al-Mg-Si alloys
-
- KANEKO Junichi
- National Research Institute for Metals College of Industial Technology, Nihon University
Bibliographic Information
- Other Title
-
- 加工熱処理したAl‐Mg‐Si合金の時効硬化挙動
- カコウ ネツ ショリシタ Al Mg Si ゴウキン ノ ジコウ コウカ キョ
Search this article
Abstract
Age-hardening behavior in final aging of TMT, in which plastic deformation is applied after pre-aging but prior to final aging, has been studied. The hardening behavior in this type of TMT is in general correlation with that in two-step aging. The strength of TMT materials increases with rising pre-aging temperature. The amount of age-hardening is degreased by plastic deformation prior to final aging due to heterogeneous precipitation on dislocations. Pre-aging prior to plastic deformation is more effective in increasing the maximum hardness in final aging than in two-step aging. This is attributed to retardation of heterogeneous precipitation on dislocations. In commercial 6061 alloy, the strength can be increased by TMT as high as 10% in contrast to the high purity alloy of the same Mg2Si content. Such differences in two-step aging and TMT behaviors between high purity and commercial alloys are attributed to metallographic heterogeneity existing in the latter.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 27 (8), 384-390, 1977
The Japan Institute of Light Metals
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206340943616
-
- NII Article ID
- 130004207941
- 10003795699
-
- NII Book ID
- AN00069773
-
- COI
- 1:CAS:528:DyaE1MXkt1CnsA%3D%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL BIB ID
- 1838680
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed