- Effect of Heat Treatment on the Pitting Corrosion Resistance of 29Cr-4Mo-2Ni Ferritic Stainless Steel
- 29Cr 4Mo 2Ni フェライトケイ ステンレス コウ ノ タイ コウショ
この論文をさがす
抄録
The effect of heat treatment on the pitting corrosion resistance of 29Cr-4Mo-2Ni ferritic stainless steel was investigated. The results as follows.<br>(1) The optimum heat treatment of 29Cr-4Mo-2Ni steel is heating at 1000°C and water quenching. In case of addition of Nb and Ti, it is heating at 1100°C and water quenching.<br>(2) In high chrominum ferritic stainless steel, carbon and nitrogen are normally controlled less than 300ppm in the total, but in this investigation a favourable pitting corrosion resistance can be obtained by heating at 1000°C and water quenching even if it contains such a high amount as 770ppm.<br>(3) In case of heating at temperature over 1100°C, there occurs sensitization by the grain boundary precipitation of Cr23C6 and Cr2N and accordingly, the pitting corrosion resistance gets deteriorated.<br>(4) In case of heating up to 800-900°C there occurs precipitation of σ phase and due to lack of Cr and Mo in α phase the pitting corrosion resistance gets deteriorated. The degree of deterioration is not influenced by the amount of carbon and nitrogen, but there is a tendency that it gets rather big by the addition of Nb or Ti.
収録刊行物
-
- 電気製鋼
-
電気製鋼 50 (4), 272-279, 1979
大同特殊鋼株式会社
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206386311040
-
- NII論文ID
- 130000743067
-
- NII書誌ID
- AN00152276
-
- ISSN
- 18834558
- 00118389
-
- NDL書誌ID
- 2069141
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可