磁石・半導体　　高性能ラジアル異方性Ｎｄ‐Ｆｅ‐Ｂ磁石

DOI Web Site 被引用文献1件

書誌事項

タイトル別名
  • Magnets and Semiconductor Devices. High Performance Radially-Oriented Nd-Fe-B Magnet.
  • 高性能ラジアル異方性Nd-Fe-B磁石
  • コウセイノウ ラジアル イホウセイ Nd-Fe-B ジシャク

この論文をさがす

説明

High Performance Radially-Oriented Nd-Fe-B Magnet Takahiko Iriyama, Norio Yoshikawa, Hiyoshi Yamada, Yasuaki Kasai Radially-oriented Nd-Fe-B magnets with (B H)max of 29 ~ 37 MGOe have been produced by hot extrusion of isotropic fully dense magnets made from melt spun powder. The key factors which enhance the (B H)max are the volume fraction and the orientation of magnetic phase (Nd 2 Fe 14 B phase). The orientation of Nd 2 Fe 14 B crystals, which occurs during the hot extrusion, depends on the hot workability of the material. Therefore, in addition to the magnetic properties, the hot workability has been investigated in the material with the composition of 29.0 ~ 32.0 wt% Nd-0.82 ~ 1.03 wt% B-balance Fe-6 wt% Co-0.6 wt% Ga in order to develop the higher (B H)max magnet. The following results were obtained: 1. A good hot workability was observed in the wide composition range except for the composition range of Nd < 30 wt% and B > 0.95 wt%. 2. A (B H ) m a x over 40 MGOe was obtained for the magnet with the composition of 29.0 ~ 29.8 wt% Nd- 0.90 ~ 0.95 wt% B-balance Fe-6 wt% Co- 0.6 wt% Ga by hot extrusion at 800 °C. 3. The newly developed radially-oriented magnet (ND-39R) had the comparable thermal-coefficients of B r and i H c to the conventional magnets (ND-35R and ND-31HR), and its excellent practical property for motors was also confirmed by flux-density evaluation with the sample magnetized

収録刊行物

  • 電気製鋼

    電気製鋼 69 (4), 219-227, 1998

    大同特殊鋼株式会社

被引用文献 (1)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ