- Preparation of Heat- and Alkali-resistant Anion-exchange Membranes by Electron-beam-induced Graft Polymerization of Bromo-butyl Styrene onto Polyethylene Film
- ブロモブチルスチレン ノ ポリエチレン フィルム エ ノ デンシセン グラフト ジュウゴウ ニ ヨル タイネツセイ オヨビ タイアルカリセイ インイオン コウカン マク ノ サクセイ
この論文をさがす
抄録
Bromo-butyl styrene (BBS) was graft-polymerized onto a high-density polyethylene film with a thickness of 35 μm, previously irradiated with an electron beam. The BBS-grafted film was converted into a strongly basic anionexchange membrane (BBS-TMA membrane) by reacting with trimethylamine hydrochloride. The thickness and resistance of the BBS-TMA membrane with a BBS grafting degree of 140% and a TMA group density of 2.2 mol/kg were 50 μm and 0.57 Ωcm2, respectively, in 0.50 M sodium chloride at 298 K. After 42-day immersion of this membrane in 5.0 M NaOH at 353 K, the transport number of the BBS-TMA membrane decreased by 1.6% to 0.925 from its initial value of 0.94.
収録刊行物
-
- 膜
-
膜 35 (6), 305-310, 2010
日本膜学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206421990784
-
- NII論文ID
- 10027742041
-
- NII書誌ID
- AN0023215X
-
- ISSN
- 18846440
- 03851036
-
- NDL書誌ID
- 10914143
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可