1.2mass%N高窒素ステンレス鋼の摩擦圧接

書誌事項

タイトル別名
  • Friction Welding of 1.2mass%N High Nitrogen Stainless Steel

抄録

Recently high nitrogen steels (HNS) are known as advanced materials. Nitrogen alloying gives several beneficial effects on the many properties of steels. However, nitrogen loss unavoidably occurs when HNS is welded with fusion welding process, resulting in the reduction of corrosion resistance as well as mechanical properties. Friction welding is a solid-state joining process, and materials do not melt at the bonding interface. Hence defects associated with melting-solidification phenomena, such as nitrogen loss, weld porosity and weld cracking, do not take place. The objective of the present study is to evaluate the weldability of friction welding of high nitrogen stainless steel contained 1.2mass% nitrogen.

収録刊行物

  • 高温学会誌

    高温学会誌 35 (3), 137-141, 2009

    一般社団法人 スマートプロセス学会 (旧高温学会)

参考文献 (6)*注記

もっと見る

詳細情報 詳細情報について

  • CRID
    1390001206429517568
  • NII論文ID
    130004471223
  • DOI
    10.7791/jhts.35.137
  • COI
    1:CAS:528:DC%2BD1MXhtVWlsrzI
  • ISSN
    03871096
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ