- WANIBE Yoshimoto
- Faculty of Engineering, Nagoya University
-
- SAWADA Kohji
- Faculty of Engineering, Nagoya University Nanzan High School
-
- FUJISAWA Toshiharu
- Faculty of Engineering, Nagoya University
-
- SAKAO Hiroshi
- Faculty of Engineering, Nagoya University
この論文をさがす
説明
Since the co-existence of a small amount of tellurium can be expected to improve the practical deoxidation of steel, three kinds of experimental examinations were carried out to eliminate the residual tellurium out of steel as the subsequent treatment. The results are<br>(1) Tellurium evaporates fairy fast out of the molten iron into Ar stream.<br>(2) Rare earth metal is the best substance to be added for the elimination of tellurium at a low oxygen potential of molten iron.<br>(3) CaF2-CaGN2 composite flux is also applicable, especially one with a composition ratio of 1:1 which has succeeded in reducing the residual concentration of tellurium to rd. 20ppm (about 90% reduction performance) during 20min treatment.
収録刊行物
-
- Transactions of the Iron and Steel Institute of Japan
-
Transactions of the Iron and Steel Institute of Japan 21 (7), 512-517, 1981
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206453779456
-
- NII論文ID
- 130003456571
-
- ISSN
- 18811183
- 00211583
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可