- Tensile Strength and Elongation of Aluminum-Magnesium Alloys under Dynamic Loading. (Behavior of Aluminum-Magnesium Alloys under Dynamic Loading, 2nd Report)
- ショウゲキ カジュウ カ ニ オケル アルミニウム-マグネシウム ゴウキン タケッショウタイ ノ ヒッパリ ツヨサ , ノビ ニ ツイテ
この論文をさがす
抄録
The tensile strength and the elongation of aluminum-magnesium alloys (0.86, 2.05 and 4.75%Mg) were studied under dynamic and static loadinng at room temperature. Dynamic loading gave larger tensile strength than static test, by 25% for 0.86%Mg alloy, by 15% for 2.05%Mg alloy and 5% for 4.75%Mg alloy. The specimen with fine grains showed larger tensile strength than that with coarse grains for all the alloys under both static and dynamic test. At dynamic test, a larger value of elongation to fracture was obtained. This phenomenon was interpreted as due to the lack of time during deformations for magnesium atoms to migrate to dislocations and to pin down them. The above interpretation was consistent with the absence of multiple yielding at dynamic test, as previously reported by the authors.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (8), 549-551, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206480855552
-
- NII論文ID
- 130007332226
- 40018258154
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153594
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可