- Study of Tempering of Quenched Carbon Steel by Specific Heat Measurement
- ヒネツ ソクテイ ニ ヨル タンソ コウ ノ ヤキモドシ キコウ ノ ケンキュウ
この論文をさがす
抄録
The specific heat changes of quenched carbon steels (0.51∼1.39%C) were continuously measured in a temperature range from −100° to 600°C, using the Nagasaki-Takagi type of adiabatic calorimeter. The effect of aging was also studied. Heat evolutions due to the transformations of quenched carbon steel by tempering were observed below 500°C. A heat evolution was found to take place even at −100°C. Analysis of the specific heat-temperature diagrams shows that there are five stages of transformation in tempering of quenched carbon steel. The preliminary heat evolution begins below −100°C and finishes at about 100°C. The decomposition of martensite occurs at 100°∼160°C, and the decomposition of low carbon martensite takes place in a wide temperature range from 160° to 500°C. The retained austenite decomposes at 200°∼300°C, while the ε-carbide decomposes at 300°∼400°C. No χ-carbide seems to be precipitated in tempering of quenched carbon steel.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (8), 494-498, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206480874240
-
- NII論文ID
- 130007332248
- 40018258157
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153597
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可