二次元周期構造を有する Co-Pt 反強磁性結合積層体の磁気特性

DOI Web Site Web Site 参考文献34件

書誌事項

タイトル別名
  • Magnetic Properties of Antiferromagnetically Coupled Co-Pt Stacked Films with Two-Dimensional Array Structures
  • 二次元周期構造を有するCo-Pt反強磁性結合積総層体の磁気特性
  • ニジゲン シュウキ コウゾウ オ ユウスル Co-Pt ハン キョウジセイ ケツゴウ セキ ソウ ソウタイ ノ ジキ トクセイ

この論文をさがす

抄録

  The influence of two-dimensional nano-structures on magnetic properties has been investigated in perpendicular antiferromagnetically coupled (AFC) Co80Pt20 stacked films. The AFC-samples consisted of [Co-Pt(10 nm)/Ru(0.46 nm)/Co-Pt(5 nm)] stacked layers, and the magnetization of the 5-nm-thick bottom Co-Pt layers was firstly reversed by AF-coupling. Hexagonal arrays of dots and holes were formed on both (top and bottom) Co-Pt layers and only on the top Co-Pt layer. The interlayer exchange coupling between the top and bottom Co-Pt layers across very thin Ru interlayer of 0.46 nm in thickness was kept even after the nanofabrication of about 100 nm in diameter. The coercivity of dot arrays markedly increased with a decrease in dot diameter, while the magnetic properties of hole arrays were less influenced by the nanoscale patterning. The magnetization rotation of AFC-samples with the patterned top layer changed from multiple to continuous reversal processes with decreasing in patterning size. For the top layer patterned sample, the minor loop shift of the 100-nm-dot arrays decreased from 240 to 140 kA/m, while the 100-nm-hole arrays showed almost the same strength of interlayer exchange coupling compared with that of continuous film prior to patterning.<br>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 77 (10), 419-423, 2013

    公益社団法人 日本金属学会

参考文献 (34)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ