抄録
During β→α transformation of a Cu-Al alloy containing about 9%Al, segregation of solute atoms was found to occur in a similar manner as the segregation which occurs during solidification of alloys. The amount of (α+δ) eutectoid caused by the segregation increased at greater rates of cooling from 975°C. A long-time annealing at 975°C, the β phase range of the alloy, resulted in large grain sizes of α phase, which caused much segregation of solute atoms. The effect of cooling rate on the amount of segregation during solid-solid transformation was compared to that of rate of solidification on the amount of the segregation during liquid-solid transformation. But the effect of α-grain size on the amount of segregated eutectoid was attributed to the rate of nucleation of α within β phase.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (6), 344-348, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206480996736
-
- NII論文ID
- 40018258119
- 130007332393
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153559
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可