- Effect of Heat-Treatment on the Mechanical Properties of Nodular Graphite Steel Castings (Study on Nodular Graphite Steel. 1st Report)
- キュウジョウ コクエン コウ ノ キカイテキ セイシツ ニ オヨボス ネツ ショリ ノ エイキョウ
この論文をさがす
抄録
It has been found that nodular graphite steel may be more readily obtained in the as-cast condition by addition of a suitable iron-calcium base alloy to molten steel of hypereutectoid composition and of lower silicon content. Steel samples containing 1.1∼1.5%C were melted in a magnesia-lined high-frequency induction furnace. The melt was divided into two or three parts, each part being treated with 0.8 or 2.0% of the iron-calcium base alloy and cast into a CO2 sand mould or a dry sand mould of keel block type. After various heat treatments, test pieces were machined from these steel castings. The result of this experiment may be summarized as follows: (1) The mechanical properties of nodular graphite steel castings in the heat-treated condition were better than those of the as-cast condition. The specimens with spheroidized pearlite structure showed high tensile strength and high ductility such as tensile strength of 70∼85 kg/mm2 and elongation or reduction of area of about 10% respectively. (2) With increasing carbon contents, the ratio of graphitization increased and the specimens with ferrite structures showed stronger graphitization than those with any other structures.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (7), 456-461, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206480999296
-
- NII論文ID
- 40018258133
- 130007332396
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153573
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可