- The Chemical Compositions and Self-Annealing of High-Manganese-Aluminium-Bronze Castings
- コウマンガン アルミニウム セイドウ ノ ゴウキン セイブン ト ジコ ショウドン ニ ツイテ
この論文をさがす
抄録
It is well known that the embrittlement (so-called self-annealing) of Al-bronze containing β phase is caused by the transformation β→α+γ2 at slow cooling, and on adequate Mn addition to Cu-Al alloys causes the β phase to stabilize. Then we tried to obtain a chemical composition of Al-Bronze containing β phase for large castings showing no self-annealing by stabilizing β phase. At first, studying the mechanical properties of slow-cooled castings of Cu-Al-Mn system (Al5∼12%, Mn0∼14%), it became known that (α+β) Al-bronze containing 6∼14% of Mn in addition would not undergo self-annealing at slow cooling. Then we improved the mechanical properties of Cu-Al-Mn system by Ni and Fe addition, and obtained the alloys for large castings consisting of the following composition:<BR>(This article is not displayable. Please see full text pdf.) <BR>Such Mn-Al-bronzes have excellent proof stress, corrosion resistance to sea water, and show as little change in mechanical properties by variation of the cooling rate as Ni-Al-bronze.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (6), 402-406, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481007872
-
- NII論文ID
- 130007332417
- 130007332407
- 40018258056
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153496
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可