- Observations on the Particle Distribution of Titanium-Carbide Powder
- TiC フンマツ ノ リュウド ブンプ ニ カンスル カンサツ
この論文をさがす
説明
In order to elucidate the physical properties of titanium-carbide powder is fabricated by the method of arc melting and crushed by a stamp mill and a ball mill, the particle distribution and their size and shape were observed as the first step of the study. The following results were obtained: (1) The finest particles, which were sifted with an infrasizer and have the mean size of 0.1 μ increased up to 70 wt% under the air pressure of 0.2 kg/cm2 at the duration time of 18 hrs. (2) The largest particles which have the mean size of 15 μ, decreased to 4 wt% under the same condition (3) Particles having the angles of 60°, 90° and 120°C were observed by the electron-microscope. This means that the pulverization is preferantially effected along the (100) and the (111) planes of the crystal.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (5), 312-315, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481096704
-
- NII論文ID
- 130007332498
- 40018257681
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153121
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可