書誌事項
- タイトル別名
-
- Study of Age-Hardening of Soft Steel by Means of High-Temperature Hardness Meter
- コウオン コウドケイ ニ ヨル ナンコウ ノ ワイ ジコウ コウカ ノ ケンキュウ
この論文をさがす
抄録
The phenomenon which is called strain-aging reaction—the hardening of metal by aging reaction after cold working—brings us face to face with various problems. It was confirmed that strain-age hardening is caused by C and N dissolved in α iron, and the phenomenon in consequence of fixing C or N as TiC or TiN by can be nearly totally prevented adding proper amount of Ti, and extremely decreasing the amount of C or N dissolved in α iron. But there is no definite theory on the influence of small amount of C or N dissolved in α iron on strain-aging reaction. In our research in connection with the age hardening phenomenon, the hardness of mild steel was measured at various temperature in the range from room temperature to 340°C, using specimens of 0.07%C steel, in which were the amount of C or N being dissolved in α iron was variously increased or decreased by heat treatment. As the result it was found that the 1st peak of hardness occured by coagulation of C or N in the vicinity of the dislocation at various temperature below 200°C according to the solubility of C or N in α iron, and the 2nd peak was caused by recovery of N in α iron at temperature from 210°C to 240°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (2), 86-91, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481174784
-
- NII論文ID
- 40018258057
- 130007332573
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153497
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可