- 寺沢 正男
- 武蔵工業大学工学部
書誌事項
- タイトル別名
-
- On The Creep Resistance of Lead-Silicon and Lead-Antimony-Silicon Alloys
- Pb-Si オヨビ Pb-Sb-Si ゴウキン ノ タイクリープセイ ニ ツイテ
この論文をさがす
抄録
In this paper, the change in creep resistance of lead and lead-antimony alloys due to silicon content is described. Specimens used in this study were extruded wires of 2 mm diameter and the testing temperature was from 29 to 31°C. The results obtained were as follows: (1) The creep resistance properties of lead and lead-antimony alloys were improved by addition of silicon. An increase of silicon and antimony content in lead seemed to increase the creep resistance at high stress. (2) The creep rate in 100 hrs of lead and its alloys was decreased generally by addition of silicon. (3) The time required for 1% elongation in lead-silicon alloys was longer than in lead, in lead-antimony-silicon alloys was generally longer than in lead-antimony alloy and the value at low stresses was similar to that of lead.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (1), 8-11, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481209344
-
- NII論文ID
- 40018258001
- 130007332612
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153441
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可