- The Effect of P on the Properties of 18Cr-10Ni-0.5W-0.5Mo-0.25Cb-Type Austenitic Stainless Steel. (Study on High Yield Strength Stainless Steel, (1))
- 18Cr-10Ni-0.5W-0.5Mo-0.25Cbケイ オーステナイト ステンレス コウ ニ オヨボス P ノ エイキョウ
この論文をさがす
抄録
The effect of phosphorus on the properties of 18Cr-10Ni-0.5W-0.5Mo-0.25Cb-type austenitic stainless steels with or without addition of nitrogen was studied. The results obtained were as follows: (1) Phosphorus increased the maximum hardness obtained by aging after quenching from 1150°C. The austenitic steel containing 0.23%C; 0.26%P and 0.15%N had a yield strength (0.2%) of 90 kg/mm2, elongation of 22% and low magnetic permeability of 1.003 in the hardened condition. (2) Against boiling 40%HNO3 and boiling 20%CH3CO2H solution, the austenitic steel containing phosphorus had good corrosion resistance in the hardened condition, although the corrosion loss was increased slightly with increase of the phosphorus and carbon contents.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (1), 65-70, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481211264
-
- NII論文ID
- 40018257998
- 130007332616
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153438
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可