- 沼倉 健一
- 東北大学金属材料研究所
書誌事項
- タイトル別名
-
- Study on Hot-Rolled “Alfer” Sheets Subzero-Quenched in Liquid Nitrogen
- コウオン アツエン サレタ アルフェル ゴウキン ノ テイオン ヤキイレ
- Study on Hot-Rolled “Alfer” Sheets Subzero-Quenched in Liquid Nitrogen
この論文をさがす
抄録
Hot-rolled “Alfer” sheets containing 12.29 per cent of aluminum were heated for one hour at some temperatures from 300°C to 1200°C, then quenched in liquid nitrogen from the heating temperature, and the magnetostriction, the Young’s modulus and the saturation magnetization were measured. In general, the saturation magnetostriction decreased almost linearly to a minimum at 500°C with rise of quenching temperature from 300°C to 500°C, then increased slowly with rise of quenching temperature. On the contrary, the Young’s modulus generally increased to a maximum at 500°C with rise of quenching temperature, then decreased abruptly, and showed again the tendency of slight increase above 800°C, although there was a minimum at 450°C at 0° or 90° to the roll direction. The saturation magnetization decreased to a minimum at 450°C, but increased abruptly at 500°C, then showed the tendency of slightly increasing until the quenching temperature at 800°C, and decreased again at 1000°C. From the results obtained, it may be inferred that the effect of thermal stress caused by the above subzero quenching is largest at 500°C, and becomes smaller at the temperatures above or under 500°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (1), 1-4, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481244416
-
- NII論文ID
- 130007332674
- 40018258008
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153448
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可