- Cu-Si-Zn合金状態図に関する研究 とくにγ固溶体付近について
- Cu-Si-Zn ゴウキン ジョウタイズ ニ カンスル ケンキュウ トクニ ガンマ コヨウタイ フキン ニ ツイテ
- Study of the Diagram of Cu-Si-Zn Alloy, On the Range Near γ Solid Solution
Search this article
Abstract
The Cu-Si-Zn alloys in the composition near Cu 45 wt%, Si 5 wt% and Zn 50 wt% (γ solid solution) were investigated by means of thermal analysis and microscopic examination. A transformation of the γ solid solution, γ\ ightleftarrowsγ′, was found below 457°C in a range of the ternary system, and the transformation temperature lowers with decrease of Si content in the solid solution. This transformation may proceed by a diffusionless mechanism and the low temperature phase γ′ seems to have a distorted γ-brass type structure. The twin-like figure appeared in the γ′ phase of the slowly cooled specimens is attributed to the transformation from γ to γ′.<BR>By measurements of electrical resistance of the alloys near the β solid solution, it was found that Si has little effect on the temperature of the order-disorder transformation in the β solid solution.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 27 (8), 370-376, 1963
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206481280128
-
- NII Article ID
- 130007332745
- 40018258274
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153714
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed