- On Each Phase Composition of TiC-Ni Cermet
- TiC-Ni サーメット ノ カク ソウ ノ ソセイ ニ ツイテ
この論文をさがす
抄録
Each phase of TiC-Ni cermet was studied by means of electrolytic separation and chemical analysis, X-ray diffraction and micro-hardness measurement, with the following results:<BR>The solubility of TiC in Ni phase was determined to be 2.7Ti+C, 3.4Ti+C and 5.3Ti+C (in wt%) at 1200°, 1250° and 1300°C, respectively. Although it is considered that Ti dissolves substitutionally in Ni and C dissolves interstitially in it, but the content of C in the solid solution is considerably small as compared with that of Ti. Thus, it is reasonable to consider that free C is present in the phase of the vertical section between Ni and stoichiometric TiC in the Ni-Ti-C system. And it appears that Ni dissolves substitutionally in TiC.<BR>The lameller deposit observed in about 90%Ni composition is TiC (a0=4.317 Å). The micro-hardnesses (Hv, 25 g Load) of the Ni and TiC phases were measured to be about 280 kg/mm2 and about 3200 kg/mm2, respectively.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 31 (1), 1-5, 1967
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481316992
-
- NII論文ID
- 40018256051
- 130007332799
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8371374
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可