- Studies on Hot-Pressing of TiC-Co Cermets
- TiC-Co サーメット ノ ホットプレスホウ ニ ツイテ
この論文をさがす
抄録
The mechanical properties, the density and the microstructure of TiC-Co cermets containing 20 to 60 wt% of Co, hot-pressed at temperature ranging from 1550° to 1750°, and at pressure of 20 to 140 kg/cm2 for 2 to 15 min were investigated and the relationship between the properties of cermets and the hot-pressing conditions, and also the applicability of this sintering process, were described. The main results obtained were as follows: (1) For example, powders mixed with 30 to 40 wt% of Co could be hot-pressed under condition of 1700°×(20∼50) kg/cm2×5 min. (2) The values of transverse rupture strength, hardness, density and mean grain size of carbide were 120∼130 kg/mm2, 85∼87 RA, 5.4∼5.5 g/cc and about 3 μ respectively. (3) But even under such favorable conditions, squeezing out of binder was so extreme that the maximum metal binder content of cermets successfully hot-pressed was thought to be below about 30 wt%.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (10), 618-622, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481478528
-
- NII論文ID
- 130007332927
- 40018257565
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153005
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可