The authors studied systematically the recrystallization behaviour of pure chromium of 99.9% purity produced by the electrolysis of chromic acid and obtained the following results: (1) The primary recrystallization behaviour of high-purity chromium was observed to follow the wellknown general rules of recrystallization. (2) The minimum amount of working necessary for producing primary recrystallization was about 10% of reduction by rolling. (3) The activation energies for recrystallization were measured as 100 to 112 kcal/mol by isothermal measurements for specimens which were subjected to 73% reduction. (4) Grain growth due to boundary migration was observed during annealing above 1000°C for specimens which were subjected to 6∼9% reduction.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (11), 760-764, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481552640
-
- NII論文ID
- 130007333046
- 40018257596
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153036
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可