- The Effect of Shot-Peening Against Stress-Corrosion Cracking of Austenitic Stainless Steels (Study on Stress-Corrosion Cracking of Austenitic Stainless Steels, 1st Report)
- オーステナイト ステンレス コウ ノ オウリョク フショク キレツ ニ タイスル ショット ピーニング ノ コウカ ニ ツイテ
この論文をさがす
抄録
Assuming that shot-peening leaves compressional stress on metallic surface and may cancel out the harmful tensile stress, the effect of this operation against stress-corrosion cracking of stainless steels was investigated experimentally. A weak peening was practically ineffective, but beyond a degree of peening, stress-corrosion cracking was reduced. A fair success was achieved at the level of peening where “coverage” was 90∼100%, and “archeight” was 0.013∼0.015 A. It is supposed that the uneveness of shot-peened surface may be harmful from the standpoint of general corrosion, but the corrosion resistance of shot-peaned stainless steels did not deteriorate except in corrosive environments which were capable to activate stainless steels.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (12), 786-790, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481560960
-
- NII論文ID
- 130007333064
- 40018257609
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153049
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可