書誌事項
- タイトル別名
-
- On the Length Changes in Hot-Bath Quenching at Low Temperatures and Aging at Room Temperature of Eutectoid Carbon Steel (Hot-Bath Quenching at Low Temperatures of Eutectoid Carbon Steel, 3rd Report)
- キョウセキ タンソ コウ ノ テイオン ネツヨク ヤキイレ オヨビ ジョウオン ジコウ ニ ヨル ナガサ ノ ヘンカ
この論文をさがす
抄録
The length changes in hot-bath quenching both above and below the Ms temperature and aging at room temperature as well as in tempering of a 0.8%C steel were measured. The experiment has revealed the following: The expansion in hot-bath quenching at the martensitic range, of 200°C-1 hr or 180°C-5 hr, in which a mixed structure of lower-bainite and tempered martensite containing a lot of retained austenite is formed, is much smaller than that in ordinary quenching or martempering, and then, during the subsequent aging at room temperature a comparatively large expansion occurs with time in these hot-bath quenched specimens as a part of the retained austenite decomposes into martensite. The retained austenite is more stabilized in consequence of the proceeding of the lower-bainite reaction, but does not decompose at room temperature, causing little change in length.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (12), 782-785, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481561728
-
- NII論文ID
- 40018257616
- 130007333066
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153056
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可