Fe-C-Si系合金および鋳鉄からの常温における水素の逸出について

DOI Web Site Web Site

書誌事項

タイトル別名
  • Evolution of Hydrogen from Fe-C-Si Alloy and Cast Iron at Room Temperature. (Studies on Determination of Hydrogen in Cast Iron, 1st Report.)
  • Fe-C-Siケイ ゴウキン オヨビ チュウテツ カラ ノ ジョウオン ニ オケル スイソ ノ イッシュツ ニ ツイテ

この論文をさがす

抄録

Small rectangular specimens (6×6×50 mm) were chill-cast in a copper mould from molten Fe-C-Si alloys (C 0.04∼4.43%, Si 0.14∼3.65%) and molten commercial cast iron. The rate of evolution of hydrogen at room temperature from these specimens were measured by placing them in test tubes filled with mercury or in evacuated tubes. In general, the specimens containing higher carbon and silicon had considerably slower rate of evolution. The hydrogen evolution from the specimens with high carbon and silicon content was too slow to be measured by the test tubes filled with mercury, but all the specimens tested in the evacuated tubes evolved hydrogen. A 95% value period which is the time required for evolution of 5% of initially contained hydrogen was used to indicate the rate of hydrogen evolution. The 95% value period for steel, malleable cast iron and ordinary cast iron were 0.6∼2.2 hrs, 22∼70 hrs and 70∼167 hrs, respectively. A drop of temperature was effective in slowing hydrogen evolution, and the 95% value period of the specimen in ice was lengthened to about twice of that of the specimen at room temperature.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 24 (11), 703-707, 1960

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ