書誌事項
- タイトル別名
-
- Effect of Cold Working on Corrosion of Stainless Steel in High Temperature Water
- ステンレス コウ ノ コウオンスイ フショク ニ オヨボス レイカン カコウ ノ エイキョウ
この論文をさがす
抄録
The effect of cold-working on corrosion of AISI type 304(or 304L) stainless steels were investigated in high-purity water at 300°C under pressure of 87 kg/cm2. An X-ray diffractometer used to investigate the ferrite formation caused by cold-working. The corrosion results were compared with the corrosion in boiling 65% nitric acid and in boiling copper sulfate-sulfuric acid solution. The results are summarized as follows: (1) The degree of cold working does not seem to have a direct relation to the corrosion resistance of type 304 (or 304L) stainless steel in high temperature water and in boiling 65% nitric acid. (2) The ferrite produced by cold-working accelerates the corrosion in high temperature water. However, the ferrite does not seem to affect the corrosion resistance in boiling 65% nitric acid and in boiling copper sulfate-sulfuric acid solution. (3) The tensile strength measurement indicate the existence of the intergranular attack in high carbon specimens after the test in boiling copper sulfate-sulfuric acid solution. However, no evidence of intergranular attack is found in high temperature water.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (9), 616-621, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481679488
-
- NII論文ID
- 40018258164
- 130007333283
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153604
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可