- Soeno Kô
- Hitachi Research Laboratory, Hitachi Ltd.
-
- Tuchiya Masatosi
- Hitachi Research Laboratory, Hitachi Ltd.
Bibliographic Information
- Other Title
-
- Fe-Co-NおよびFe-Ni-N合金の内部摩擦
- Fe-Co-N オヨビ Fe-Ni-N ゴウキン ノ ナイブ マサツ
Search this article
Abstract
Nitrogen diffusion peaks of iron alloys containing less than five atomic pct cobalt or nickel were measured with a torsion pendulum of about Ic/s and with a transverse vibration mode of about 350 c/s. Observed peaks in Fe-Co-N and Fe-Ni-N alloys are very similar to the usual nitrogen peak of unalloyed ferrite. These elements presumably do not sensibly alter the diffusion rate of nitrogen in ferrite.<BR>Precipitation of nitrogen during isochronal annealing was investigated by the internal friction method. The results show that Fe8N phase precipitated in Fe-5 at%Co-N alloy is decreased in considerable amount. This is tentatively interpreted as the indication that the nitrogen concentration equilibrated with Fe8N is increased by the addition of cobalt.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 31 (4), 305-310, 1967
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001206481719680
-
- NII Article ID
- 130007333349
- 40018256165
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 8371479
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed