書誌事項
- タイトル別名
-
- On the “Work Softening” Phenomenon of Aluminium
- アルミニウム ノ カコウ ナンカ ゲンショウ ニ ツイテ
- On the “Work Softening” Phenomenon of Aluminium
この論文をさがす
抄録
As a result of studying the effects of the purity of aluminium and the heat-treatment on the “Work Softening” phenomenon of aluminium, it was found that this phenomenon was observed in the special state of the commercially pure aluminium.<BR>For example, 99.2% aluminium sheet annealed at 240°C after cold rolling, increased the elongation from 16 to 25% and decreased the proof stress from 12.0 to 10.6 kg/mm2 and the tensile strength from 12.5 to 11.8 kg/mm2 with reduction of 1% by cold rolling, after the annealing.<BR>This “Work Softening” phenomenon was observed in the half hard sheet of 99.2% and 99.8% aluminium annealed at the final temperature of about 240°C when cold rolled with reduction of 1 to 5%, if the ingot had been preheated at 500°C for 24 hrs. It was also observed that this phenomenon had no connection with the intermediate annealing and the anisotropy of the sheets.<BR>“Work Softening” phenomenon was not observed in 99.99% aluminium and the commercially pure aluminium obtained from the ingot not preheated.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 27 (2), 79-83, 1963
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481873792
-
- NII論文ID
- 130007333542
- 40018258216
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153656
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可