書誌事項
- タイトル別名
-
- On the Surface tension of the Molten Silicates
- ヨウユウ ケイサンエン ノ ヒョウメン チョウリョク ニ ツイテ
この論文をさがす
抄録
The surface tension of the sodium silicate-metal oxide system was measured by a sessile drop method in nitrogen flow. The sodium silicate consisted of 44.5 mol%Na2O and 55.5 mol%SiO2, and metal oxide (CaO, MgO, MnO, and Al2O3) was added by 5 mol%, 10 mol%, 15 mol% to sodium silicate. Generally, the surface tension of sodium silicate increases with the content of additional metal oxide. When sulfur was added to the sodium silicate, its surface tension decreased. The temperature coefficient of the surface tension of sodium silicate was negative, while that of the silicate containing Al2O3 was positive. The density of liquid sodium silicate was calculated based on the dimensions of the sessile drops of silicate.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (8), 453-456, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481907328
-
- NII論文ID
- 130007333603
- 40018257501
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152941
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可