- Effect of Vanadium on Properties of Age-Hardenable Mn-Cr Type Nonmagnetic Steel
- ジコウ コウカガタ Mn-Crケイ ヒジセイ コウ ノ キカイテキ セイシツ ニ オヨボス V ノ エイキョウ
この論文をさがす
抄録
The effect of containing vanadium (0∼2.7%) on the properties of 17Mn-12Cr type nonmagnetic austenite steel investigated. The results obtained were as follows.<BR>(1) Hardness, yieled strength after aging treatment increased with the vanadium content. In all the specimens different in vanadium content the highest strength after aging was obtained by aging at 700°C×7 hr.<BR>(2) The highest strength of the 17Mn-12Cr type nonmagnetic austenite steels, containing vanadium(1.1∼2.7%), aged after solution treatment, are all about 120 kg/mm2 in yield strength (0.2%), and nearly 15% in elongation. Magnetic permeabilities of these steels in aged condition are in the vicinity of 1.002.<BR>(3) The cause for hardening of these austenitic steels is the formation of particular vanadium carbide by the addition of vanadium which has a strong affinity for carbon and the remarkable precipitation of the vanadium carbide by aging for a short time after solution treatment.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 27 (10), 490-496, 1963
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206481909632
-
- NII論文ID
- 130007333605
- 40018258188
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153628
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可