書誌事項
- タイトル別名
-
- Studies on the Platinum-base Alloys in Pt-Mo System
- ハッキンキ Pt-Mo ゴウキン ノ ケンキュウ
この論文をさがす
抄録
Studies of the physical and technical properties of Pt-Mo alloys were carried out. The maximum solubility limit of Mo in α-phase (Pt-phase) is 15%, and the lattice parameter of α-phase (f.c.c.) lowers with the increase of the Mo content. Cold-working can be applied to α-phase alloys which contain less than 6% of Mo, and their annealing temperature is above 1,100°C. The oxidation of Pt-Mo alloys has been studied. At high temperature i.e., above 1,000°C, MoO3 volatilizes away as rapidly as it is formed, and the β-phase transforms into α-phase by oxidation in air. A preferred oxidation of Mo in α-phase was observed by prolonged heating in air, and it oxidized according to a logarthmic-rate law.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (10), 616-620, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482153344
-
- NII論文ID
- 40018257323
- 130007333804
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152763
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可