気相反応により生成された結晶チタンの純度並びに機械的性質

DOI Web Site Web Site

書誌事項

タイトル別名
  • On the Purity and the Mechanical Properties of Crystalline Ti Produced by the Gaseous Reaction of TiCl<SUB>4</SUB> and Mg
  • キソウ ハンノウ ニ ヨリ セイセイ サレタ ケッショウ チタン ノ ジュンド ナラビニ キカイテキ セイシツ

この論文をさがす

抄録

The purity and mechanical properties were examined experimentally on crystalline Ti produced by the reaction in the gaseous phase of TiCl4 and Mg. We found that it had a purity near that of the iodide process Ti by chemical analysis. Even if a slightly low grade of TiCl4 or Mg was used as the raw material, high purity Ti was obtained owing to the distillation effect followed by the evaporation of TiCl4 and Mg. The possibility of admixture of Fe from the construction materials of the reaction vessels was specially studied, but it was found that the admixture of Fe was extremely reduced by using a graphite lining on the inner surfaces of leading pipes of TiCl4 and Ti-coated frames and sleeves. Iron contamination can occur in the case of excess TiCl4 which may be caused by the fluctuation of the flow rate of both vapours, therefore when the control of the flow rate is kept precisely constant the admixture of Fe could be kept below 0.01%. The hardness of crystalline Ti produced at our laboratory was in the range of 82 to 100 in V.H.N and 85 in the average. Tensile and Charpy impact tests were carried out and we obtained 30∼35 kg/mm2 in tensile strength, 13∼20 kg/mm2 in yield strength, 84∼82% in reduction of area and 60∼58% in elongation. It was shown that the crystalline Ti has excellent mechanical properties of high ductility in spite of slightly higher strength than the iodide process Ti. In the impact tests the test specimens with V notch and U notch were not broken even in the low temperature range of liquid nitrogen, and it was shown that the impact value of crystalline Ti was higher as the temperature was lowered.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 23 (11), 637-641, 1959

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ