- On the Variation of Young’s Modulus (<I>E</I>) of 65-35 Brass Resulting from Rolling and Annealing
- 65-35 オウドウ ノ レイカン アツエン ト ショウドン ニ ヨル ヤングリツ ノ ヘンカ ニ ツイテ
- On the Variation of Young’s Modulus (<I>E</I>) of 65-35 Brass Resulting from Rolling and Annealing
この論文をさがす
抄録
The variation of Young’s modulus of 65-35 brass resulting from cold-rolling and annealing has been studied by means of longitudinal-vibration method. The results obtained are as follows: (1) The variation of E resulting from cold-rolling was the same as that of 7-3 brass in all measuring directions. (2) The variation of E resulting from annealing showed various features according to the annealing temperature, the degree of rolling (reduction) and the measuring direction. (3) The anisotropy of E resulting from 30∼40%-rolling disappeared by annealing above the recrystallization temperature. (4) The anisotropy of E resulting from full annealing at 600°C, 700°C, after cold-rolling was different in the case of over 90% reduction as compared with the case of reduction to 80%. (5) The anisotropy of E resulting from annealing after over-90%-reduction was almost the same as that obtained before annealing excepting the case of 450°C annealing. (6) In the case of over-90%-reduction, the anisotropy of E resulting from 450°C annealing was different from that obtained by annealing at above 600°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 23 (10), 573-576, 1959
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206482157440
-
- NII論文ID
- 130007333812
- 40018257305
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152745
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可