Cu-Si-Zn合金状態図に関する研究　特にη相付近について

DOI Web Site Web Site

書誌事項

タイトル別名
  • Study of the Diagram of Cu-Si-Zn Alloy, On the Range Near η Phase
  • Cu-Si-Zn ゴウキン ジョウタイズ ニ カンスル ケンキュウ , トクニ イータソウ フキン ニ ツイテ
  • Study of the Diagram of Cu-Si-Zn Alloy, On the Range Near η Phase

この論文をさがす

抄録

The range near η solid solution of the Cu-Si-Zn system has been investigated by means of thermal analysis, measurement of electrical resistance and microscopic examination. The η solid solution, which is a Cu3Si solid solution, has two transformations of η\ ightleftharpoonsη′ and η′\ ightleftharpoonsη″. That is, the peritectoids of γ+η\ ightleftharpoonsη′ and γ+η′\ ightleftharpoonsη″ are at 620°C and 570°C and the eutectoids of η\ ightleftharpoonsη′+Si and η′\ ightleftharpoonsη″+Si are at 558°C and 467°C respectively, in Cu-Si binary system. And in the ternary system, the non-variants to ε′+η\ ightleftharpoonsγ+η′, η\ ightleftharpoonsγ+η′+Si, ε′+η′\ ightleftharpoonsγ+η″, and γ+η′\ ightleftharpoonsη″+Si are found at 600°, 530°, 500° and 480°C, respectively. The twin of the solid solution found in the cast or annealed alloys is the annealing twin attributed to the transformations.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 23 (10), 585-589, 1959

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ